2007 Volume 2007 Issue 228 Pages 158-162
We have prepared Carbon/Fe-Ni-Cu ternary alloy composites by polymerized complex method. A single-phase Fe-Ni-Cu alloy could be obtained in carbon matrix by controlling pH of the citrate complex solution. It was revealed that the chemical compositions of metals in composites were maintained well by adding ethylene glycol into the complex solution. Crystallinity of both carbon matrix and Fe-Ni-Cu alloy particles were enhanced with increasing the carbonized temperature. The composite carbonized at 700°C had larger saturation magnetization and smaller coercivity than that carbonized at 500°C, which correlated with metal content and crystallite size of alloy. The composite carbonized at 700°C exhibited larger permeability and permittivity than carbon/Fe-Co alloy composites at frequency of GHz range.