電子線後方散乱回折法による浸炭焼入鋼の 硬化層深さと残留応力の評価
坂井田 喜久稲山 朝仁矢代 茂樹
著者情報
ジャーナル フリー

2014 年 63 巻 7 号 p. 557-562

詳細
抄録

A chromium-molybdenum steel composed of 0.20 mass% carbon was used as a starting material. Two kinds of specimens having different case depths were made by carburizing and quenching. Using the scanning electron microscope, the crystallographic information was measured on the cross-sectional hardened layer by electron backscattering diffraction method. The kernel average misorientation, Θ, of the inverse pole figure were calculated from the carburized surface to the interior of each specimen. The area-average, Θmean, was compared to the case depth and the cross-sectional residual stress distribution measured by x-ray. As a result, the area-average of the hardened layer was larger than that of the interior of specimen after heat treatment. The estimated depth of the increment in the Θmean found to accord to the case depth and be proportional to the depth in which large compressive residual stress was distributed on the gradually polished surface. Therefore, the case depth and eigen strain distribution that induce the compressive residual stress can be indirectly estimated by electron backscattering diffraction method.

著者関連情報
© 2014 日本材料学会
前の記事 次の記事
feedback
Top